Ferroelectric pbzr0.2ti0.8o3 thin films on epitaxial y-ba-cu-o
Publication Type | Journal Article
|
---|
Authors | |
---|---|
DOI |
10.1080/10584589208215712
|
Abstract |
Using a combination of pulsed laser deposition and sol-gel processing, we have fabricated epitaxial PbZr0.2Ti0.8O3/YBa2Cu3O7-x heterostructures on single crystalline [001] LaAlO3- Rutherford Backscattering studies show the composition to be the same as the nominal starting composition. Transmission electron microscopy shows the existence of a randomly oriented polycrystalline microstructure in the PZT layer with a grain size of about 500–1000Å. Microscopic pores were also observed in the PZT layer. The PZT film exhibits ferroelectric hysteresis with a saturation polarization of 22–25μC/cm2 (at 7.5V, 1kHz), a remanence of 5–6μC/cm2 and a coercive field of about 40kV/cm. © 1992, Taylor & Francis Group, LLC. All rights reserved.
|
Notes |
cited By 0
|
Journal |
Integrated Ferroelectrics
|
Volume |
1
|
Year of Publication |
1992
|
Number |
2-4
|
Pagination |
205-212
|
ISSN Number |
10584587
|
Research Areas | |
Download citation |