%0 Journal Article
%K Thin films
%K Lanthanum compounds
%K Ferroelectricity
%K Interfaces (materials)
%K Dislocations (crystals)
%K Strain
%K Barium compounds
%K Crystal microstructure
%K Phase shifters
%K Film crystallinity
%K High resolution X ray diffractometry
%K Lanthanum strontium oxides
%K Paraelectric films
%A C.H Mueller
%A F.W Van Keuls
%A R.R Romanofsky
%A F.A Miranda
%A J.D Warner
%A C.L Canedy
%A Ramamoorthy Ramesh
%B Integrated Ferroelectrics
%D 2000
%G eng
%I Taylor and Francis Inc.
%P 139-149
%R 10.1080/10584580008222227
%T Characterization of (Ba0.5Sr0.5)TiO3 thin films for Ku-band phase shifters
%V 28
%X The microstructural properties of (Ba0.5Sr0.5)TiO3 (BSTO) thin films (300, 700, and 1400 nm thick) deposited on LaAlO3 (LAO) substrates were characterized using high-resolution x-ray diffractometery. Film crystallinity was the parameter that most directly influenced tunability, and we observed that a) the crystalline quality was highest in the thinnest film and progressively degraded with increasing film thickness; and b) strain at the film/substrate interface was completely relieved via dislocation formation. Paraelectric films such as BSTO offer an attractive means of incorporating low-cost phase shifter circuitry into beam-steerable reflectarray antennas. © 2000 OPA (Overseas Publishers Association) N.V. Published by license under the Gordon and Breach Science Publishers imprint.