%0 Conference Paper
%K Pulsed laser deposition
%K Electrochemical electrodes
%K Surface structure
%K Substrates
%K Ferroelectric materials
%K Permittivity
%K Thin film devices
%K Lanthanum alloys
%K Capacitors
%K Piezoelectric property
%K Thermal effects
%K Pulsed laser applications
%K Partial pressure
%K Lead alloys
%K Lead magnesium niobate lead titanate film
%K Oxide electrode
%K Scanned probe microscope
%A V Nagarajan
%A S.P Alpay
%A C.S Ganpule
%A B Nagaraj
%A S Aggarwal
%A A.L Roytburd
%A E.D Williams
%A Ramamoorthy Ramesh
%B Materials Research Society Symposium - Proceedings
%D 2000
%G eng
%I Materials Research Society, Warrendale, PA, United States
%P 505-510
%T Epitaxial PMN-PT relaxor thin films: dependence of dielectric and piezoelectric properties on film thickness
%V 596
%X The effect of substrate induced constraint and misfit strain on the structure and piezoelectric properties of epitaxial relaxor ferroelectric lead magnesium niobate-lead titanate (PMN-PT) films were investigated. Relaxor PMN-PT epitaxial 100-400 nm thick films with top and bottom oxide electrodes were grown by pulsed laser deposition on (100) LaAlO3 substrates. A systematic decrease in the temperature of the dielectric maximum with increasing film thickness was observed. This is accompanied by an increase in the room temperature relative dielectric constant. The longitudinal piezoelectric coefficient measured using a scanned probe microscope, increases by almost an order of magnitude with increasing film thickness.