%0 Journal Article
%K Thin films
%K Electron microscopy
%K Bismuth compounds
%K Ferroelectricity
%K Ferroelectric polarization
%K Magnetic moments
%K Antiferromagnetism
%K Magnetic domains
%K Photoemission
%K Antiferromagnetic domains
%K Piezoelectric force microscopy (PEM)
%K X-ray linear dichroism (XLD)
%A T Zhao
%A A Scholl
%A F Zavaliche
%A K Lee
%A M Barry
%A A Doran
%A M.P Cruz
%A Y.H Chu
%A C Ederer
%A N.A Spaldin
%A R.R Das
%A D.M Kim
%A S.H Baek
%A C.B Eom
%A Ramamoorthy Ramesh
%B Nature Materials
%D 2006
%G eng
%I Nature Publishing Group
%P 823-829
%R 10.1038/nmat1731
%T Electrical control of antiferromagnetic domains in multiferroic BiFeO 3 films at room temperature
%V 5
%X The antiferromagnetic domain structure of BiFeO3 films was imaged and changes induced in the antiferromagnetic domains on switching the ferroelectric polarization was recorded. Ferroelectric measurements confirm a large polarization value along the surface normal and magnetic measurements show a weak, saturated magnetic moment. The ferroelectric domain structure is both imaged and switched using piezoelectric force microscopy (PEM). The antiferromagnetic domain structure is studied before and after electrical poling using photoemission electron microscopy (PEEM) based on X-ray linear dichroism (XLD). Bulk BiFeO3 is a room temperature ferroelectric with a spontaneous electric polarization directed along one of the axes of the perovskite structure. Coupling between ferroelectricity and antiferromagnetism in BiFeO3 thin film is a result from the coupling of both antiferromagnetic and ferroelectric domains to the underlying ferroelastic domain structure.