%0 Journal Article
%K Diamond-like carbon films
%K Electron energy loss spectroscopy
%K Plasma bias
%K Substrate bias
%K Transmission electron microscopy
%A André Anders
%A Nitisak Pasaja
%A Sunnie H.N Lim
%A Tim C Petersen
%A Vicki J Keast
%B Surface and Coatings Technology
%D 2006
%G eng
%N 8
%P 4628-4632
%R 10.1016/j.surfcoat.2006.09.313
%T Plasma biasing to control the growth conditions of diamond-like carbon
%V 201
%1 <p>Windows and Daylighting Group</p>
%2 LBNL-59023
%8 01/2007
%X <p>It is well known that the structure and properties of diamond-like carbon, and in particular the sp<sup>3</sup>/sp<sup>2</sup> ratio, can be controlled by the energy of the condensing carbon ions or atoms. In many practical cases, the energy of ions arriving at the surface of the growing film is determined by the bias applied to the substrate. The bias causes a sheath to form between substrate and plasma in which the potential difference between plasma potential and surface potential drops. In this contribution, we demonstrate that the same results can be obtained with grounded substrates by shifting the plasma potential. This plasma biasing (as opposed to substrate biasing) is shown to work well with pulsed cathodic carbon arcs, resulting in tetrahedral amorphous carbon (ta-C) films that are comparable to the films obtained with the conventional substrate bias. To verify the plasma bias approach, ta-C films were deposited by both conventional and plasma bias and characterized by transmission electron microscopy (TEM) and electron energy loss spectrometry (EELS). Detailed data for comparison of these films are provided.</p>