TY - JOUR
AU - Ramamoorthy Ramesh
AU - A Inam
AU - W.K Chan
AU - B Wilkens
AU - K Myers
AU - K Remschnig
AU - D.L Hart
AU - J.M Tarascon
AB - Thin-film heterostructures of Bi4Ti3O 12/Bi2Sr2CuO6+x have been grown on single crystals of SrTiO3, LaAlO3, and MgAl 2O4 by pulsed laser deposition. X-ray diffraction studies show the presence of c-axis orientation only; Rutherford backscattering experiments show the composition to be close to the nominal stoichiometry. The films are ferroelectric and exhibit a symmetric hysteresis loop. The remanent polarization was 1.0 microcoulomb per square centimeter, and the coercive field was 2.0 × 105 volts per centimeter. Similar results were obtained with YBa2Cu3O7-x and Bi 2Sr2CaCu2O8+x, and single-crystal Bi2Sr2CuO6+x as the bottom electrodes. These films look promising for use as novel, lattice-matched, epitaxial ferroelectronic film/electrode heterostructures in nonvolatile memory applications.
BT - Science
DO - 10.1126/science.252.5008.944
LA - eng
M1 - 5008
N1 - cited By 190
N2 - Thin-film heterostructures of Bi4Ti3O 12/Bi2Sr2CuO6+x have been grown on single crystals of SrTiO3, LaAlO3, and MgAl 2O4 by pulsed laser deposition. X-ray diffraction studies show the presence of c-axis orientation only; Rutherford backscattering experiments show the composition to be close to the nominal stoichiometry. The films are ferroelectric and exhibit a symmetric hysteresis loop. The remanent polarization was 1.0 microcoulomb per square centimeter, and the coercive field was 2.0 × 105 volts per centimeter. Similar results were obtained with YBa2Cu3O7-x and Bi 2Sr2CaCu2O8+x, and single-crystal Bi2Sr2CuO6+x as the bottom electrodes. These films look promising for use as novel, lattice-matched, epitaxial ferroelectronic film/electrode heterostructures in nonvolatile memory applications.
PY - 1991
SP - 944
EP - 946
T2 - Science
TI - Epitaxial cuprate superconductor/ferroelectric heterostructures
VL - 252
SN - 00368075
ER -