Organic energy storage materials attract extensive attention as a potential alternative for the next generation of lithium ion batteries. However, most of the reported organic electrodes can not achieve a good balance among high capacity, high rate and long cycle-life. In this work, pyromellitic anhydride is adopted as a new anode material for lithium-ion batteries. It exhibits superior electrochemical performances compared to most of the reported organic electrodes. The pyromellitic anhydride anode is able to reversibly deliver a capacity of 1472.2 mAh g−1 at 30 mA g−1. Even at an extremely high current of 30 A g−1, the electrode still retains 562.7 mAh g−1. After a 500 electrochemical cycles at 150 mA g−1 charge and 600 mA g−1 discharge, almost no capacity loss can be observed. The good electrochemical performance of the pyromellitic anhydride anode is because of its excellent lithium conductivity capability, as well as the stable solid electrolyte interface film formed on the electrode.
BT - Journal of Power Sources DA - 10/2019 DO - 10.1016/j.jpowsour.2019.226848 LA - eng N2 -Organic energy storage materials attract extensive attention as a potential alternative for the next generation of lithium ion batteries. However, most of the reported organic electrodes can not achieve a good balance among high capacity, high rate and long cycle-life. In this work, pyromellitic anhydride is adopted as a new anode material for lithium-ion batteries. It exhibits superior electrochemical performances compared to most of the reported organic electrodes. The pyromellitic anhydride anode is able to reversibly deliver a capacity of 1472.2 mAh g−1 at 30 mA g−1. Even at an extremely high current of 30 A g−1, the electrode still retains 562.7 mAh g−1. After a 500 electrochemical cycles at 150 mA g−1 charge and 600 mA g−1 discharge, almost no capacity loss can be observed. The good electrochemical performance of the pyromellitic anhydride anode is because of its excellent lithium conductivity capability, as well as the stable solid electrolyte interface film formed on the electrode.
PY - 2019 EP - 226848 ST - Journal of Power Sources T2 - Journal of Power Sources TI - Pyromellitic dianhydride: A new organic anode of high electrochemical performances for lithium ion batteries VL - 436 SN - 03787753 ER -