TY - JOUR AU - Min Ling AU - Liang Zhang AU - Tianyue Zheng AU - Jun Feng AU - Jinghua Guo AU - Liqiang Mai AU - Gao Liu AB -

Polysulfide shuttling has been the primary cause of failure in lithium-sulfur (Li-S) battery cycling. Here, we demonstrate an nucleophilic substitution reaction between polysulfides and binder functional groups can unexpectedly immobilizes the polysulfides. The substitution reaction is verified by UV–visible spectra and X-ray photoelectron spectra. The immobilization of polysulfide is in situ monitored by synchrotron based sulfur K-edge X-ray absorption spectra. The resulting electrodes exhibit initial capacity up to 20.4 mAh/cm2, corresponding to 1199.1 mAh/g based on a micron-sulfur mass loading of 17.0 mg/cm2. The micron size sulfur transformed into nano layer coating on the cathode binder during cycling. Directly usage of nano-size sulfur promotes higher capacity of 33.7 mAh/cm2, which is the highest areal capacity reported in Li-S battery. This enhance performance is due to the reduced shuttle effect by covalently binding of the polysulfide with the polymer binder.

BT - Nano Energy DA - 01/2017 DO - 10.1016/j.nanoen.2017.05.020 LA - eng N2 -

Polysulfide shuttling has been the primary cause of failure in lithium-sulfur (Li-S) battery cycling. Here, we demonstrate an nucleophilic substitution reaction between polysulfides and binder functional groups can unexpectedly immobilizes the polysulfides. The substitution reaction is verified by UV–visible spectra and X-ray photoelectron spectra. The immobilization of polysulfide is in situ monitored by synchrotron based sulfur K-edge X-ray absorption spectra. The resulting electrodes exhibit initial capacity up to 20.4 mAh/cm2, corresponding to 1199.1 mAh/g based on a micron-sulfur mass loading of 17.0 mg/cm2. The micron size sulfur transformed into nano layer coating on the cathode binder during cycling. Directly usage of nano-size sulfur promotes higher capacity of 33.7 mAh/cm2, which is the highest areal capacity reported in Li-S battery. This enhance performance is due to the reduced shuttle effect by covalently binding of the polysulfide with the polymer binder.

PY - 2017 SP - 82 EP - 90 ST - Nano Energy T2 - Nano Energy TI - Nucleophilic substitution between polysulfides and binders unexpectedly stabilizing lithium sulfur battery VL - 38 SN - 22112855 ER -