7Li magic angle spinning nuclear magnetic resonance was used to observe coexisting cubic and tetragonal phases in Li1+xMn2O4. Cubic phase peaks are observed at 500-580 ppm vs. 1 M LiCL(aq); tetragonal phase peaks are observed around 100 ppm. Cycling Li1+xMn2O4 on the 3 V plateau does not result in significant changes in the cubic phase. A small amount of residual tetragonal phase accounting for ∼3% of the 7Li NMR intensity, however, is observed in spinel deep discharged to x=1 then returned to x=0.
BT - Electrochemical and Solid-State Letters DA - 08/2000 DO - 10.1149/1.1391180 LA - eng M1 - 10 N2 -7Li magic angle spinning nuclear magnetic resonance was used to observe coexisting cubic and tetragonal phases in Li1+xMn2O4. Cubic phase peaks are observed at 500-580 ppm vs. 1 M LiCL(aq); tetragonal phase peaks are observed around 100 ppm. Cycling Li1+xMn2O4 on the 3 V plateau does not result in significant changes in the cubic phase. A small amount of residual tetragonal phase accounting for ∼3% of the 7Li NMR intensity, however, is observed in spinel deep discharged to x=1 then returned to x=0.
PY - 2000 SP - 463 EP - 466 T2 - Electrochemical and Solid-State Letters TI - A 7Li NMR study of lithium insertion into lithium manganese oxide spinel VL - 3 ER -