Multilayer thin films of YBa2Cu3O7-δ (YBCO) were deposited in situ on yttria-stabilized zirconia (YSZ) and CeO2 intermediate layers grown using ion-assisted pulsed-laser deposition. These structures were grown on amorphous SiO2 dielectric layers. A critical current density of 3x105 A/cm2 was obtained for a YBCO film grown on SiO2-coated Haynes Alloy 230 substrate. Improvement of the critical current density was obtained below 77 K by doping the YBCO with 10% Ag. Angular magnetoresistance measurements provide further information about the texture of this film.

BT - IEEE Transactions on Applied Superconductvity DA - 06/1995 DO - 10.1109/77.402980 IS - 2 LA - eng LB - Laser N2 -

Multilayer thin films of YBa2Cu3O7-δ (YBCO) were deposited in situ on yttria-stabilized zirconia (YSZ) and CeO2 intermediate layers grown using ion-assisted pulsed-laser deposition. These structures were grown on amorphous SiO2 dielectric layers. A critical current density of 3x105 A/cm2 was obtained for a YBCO film grown on SiO2-coated Haynes Alloy 230 substrate. Improvement of the critical current density was obtained below 77 K by doping the YBCO with 10% Ag. Angular magnetoresistance measurements provide further information about the texture of this film.

PY - 1995 SP - 2007 EP - 2010 T2 - IEEE Transactions on Applied Superconductvity TI - Multilayer YBaCuO structures using ion-assisted intermediate layers VL - 5 SN - 1051-8223 ER -