TY - JOUR KW - Polymers KW - Secondary cells KW - Electrochemical electrodes KW - Additives KW - Composite materials KW - Electrical conductivity KW - Electron microscopy KW - Nanostructured materials AU - Gao Liu AU - Honghe Zheng AU - S Kim AU - Yonghong Deng AU - Andrew M Minor AU - Xiangyun Song AU - Vincent S Battaglia AB -

Fundamental electrochemical methods, cell performance tests, and physical characterization tests, such as electron microscopy, were used to study the effects of levels of the inert materials [acetylene black (AB), a nanoconductive additive, and polyvinylidene difluoride (PVDF), a polymer binder] on the power performance of lithium-ion composite cathodes. The electronic conductivity of the AB/PVDF composites at different compositions was measured with a four-point probe direct current method. The electronic conductivity was found to increase rapidly and plateau at an AB:PVDF ratio 0.2:1 (by weight), with 0.8:1 being the highest conductivity composition. AB:PVDF compositions along the plateau of 0.2:1, 0.4:1, 0.6:1, and 0.8:1 were investigated. Electrodes of each of those compositions were fabricated with different fractions of AB/PVDF to active material. It was found that at the 0.8:1 AB:PVDF, the rate performance improved with increases in the AB/PVDF loading, whereas at the 0.2:1 AB:PVDF, the rate performance improved with decreases in the AB/PVDF loading. The impedance of electrodes made with 0.6:1 AB:PVDF was low and relatively invariant

BT - Journal of The Electrochemical Society DA - 10/2008 DO - 10.1149/1.2976031 IS - 12 LA - eng LB - Batt N2 -

Fundamental electrochemical methods, cell performance tests, and physical characterization tests, such as electron microscopy, were used to study the effects of levels of the inert materials [acetylene black (AB), a nanoconductive additive, and polyvinylidene difluoride (PVDF), a polymer binder] on the power performance of lithium-ion composite cathodes. The electronic conductivity of the AB/PVDF composites at different compositions was measured with a four-point probe direct current method. The electronic conductivity was found to increase rapidly and plateau at an AB:PVDF ratio 0.2:1 (by weight), with 0.8:1 being the highest conductivity composition. AB:PVDF compositions along the plateau of 0.2:1, 0.4:1, 0.6:1, and 0.8:1 were investigated. Electrodes of each of those compositions were fabricated with different fractions of AB/PVDF to active material. It was found that at the 0.8:1 AB:PVDF, the rate performance improved with increases in the AB/PVDF loading, whereas at the 0.2:1 AB:PVDF, the rate performance improved with decreases in the AB/PVDF loading. The impedance of electrodes made with 0.6:1 AB:PVDF was low and relatively invariant

PY - 2008 SP - A887 EP - A892 T2 - Journal of The Electrochemical Society TI - Effects of Various Conductive Additive and Polymeric Binder Contents on the Performance of a Lithium-Ion Composite Cathode VL - 155 ER -