Thin films of lithium nickel oxide were deposited by pulsed laser deposition (PLD) from targets of pressed LiNiO2 powder with layered structure. The composition, structure and surface air sensitivity of these films were analyzed using a variety of techniques, such as nuclear reaction analysis, Rutherford backscattering spectrometry (RBS), x-ray diffraction, infrared spectroscopy, and atomic force microscopy. Optical properties were measured using a combination of variable angle spectroscopic ellipsometry and spectroradiometry. Crystalline structure, surface morphology and chemical composition of LixNi1-xO thin films depend strongly on deposition oxygen pressure, temperature as well as substrate target distance. The films produced at temperatures lower than 600 °C spontaneously absorb CO2 and H2O at their surface once they are exposed to the air. The films deposited at 600 °C proved to be stable in air over a long period. Even when deposited at room temperature the PLD films are denser and more stable than sputtered films. RBS determined that the best electrochromic films had the stoichiometric composition Li0.5Ni0.5O when deposited at 60 mTorr O2 pressure. Electrochemical tests show that the films exhibit excellent reversibility in the range 1.0 V to 3.4 V versus lithium and long cyclic life stability in a liquid electrolyte half cell. Electrochemical formatting which is used to develop electrochromism in other films and nickel oxide films is not needed for these stoichiometric films. The optical transmission range is almost 70% at 550 nm for 120 nm thick films.
BT - Electrochemical Society Meeting C1 -Windows and Daylighting Group
C2 - LBNL-39593 CN - LBNL-39593 CY - San Antonio, TX DA - 10/1996 LA - eng N2 -Thin films of lithium nickel oxide were deposited by pulsed laser deposition (PLD) from targets of pressed LiNiO2 powder with layered structure. The composition, structure and surface air sensitivity of these films were analyzed using a variety of techniques, such as nuclear reaction analysis, Rutherford backscattering spectrometry (RBS), x-ray diffraction, infrared spectroscopy, and atomic force microscopy. Optical properties were measured using a combination of variable angle spectroscopic ellipsometry and spectroradiometry. Crystalline structure, surface morphology and chemical composition of LixNi1-xO thin films depend strongly on deposition oxygen pressure, temperature as well as substrate target distance. The films produced at temperatures lower than 600 °C spontaneously absorb CO2 and H2O at their surface once they are exposed to the air. The films deposited at 600 °C proved to be stable in air over a long period. Even when deposited at room temperature the PLD films are denser and more stable than sputtered films. RBS determined that the best electrochromic films had the stoichiometric composition Li0.5Ni0.5O when deposited at 60 mTorr O2 pressure. Electrochemical tests show that the films exhibit excellent reversibility in the range 1.0 V to 3.4 V versus lithium and long cyclic life stability in a liquid electrolyte half cell. Electrochemical formatting which is used to develop electrochromism in other films and nickel oxide films is not needed for these stoichiometric films. The optical transmission range is almost 70% at 550 nm for 120 nm thick films.
PP - San Antonio, TX PY - 1996 SP - 54 EP - 63 T2 - Electrochemical Society Meeting T3 - Electrochemical Society Meeting TI - Electrochromic Lithium Nickel Oxide Thin Film by Pulsed Laser Deposition VL - 96-24 ER -