@article{30105,
  author = {Na Lin and Zhe Jia and Zhihui Wang and Hui Zhao and Guo Ai and Xiangyun Song and Ying Bai and Vincent S Battaglia and Chengdong Sun and Juan Qiao and Kai Wu and Gao Liu},
  title = {Understanding the crack formation of graphite particles in cycled commercial lithium-ion batteries by focused ion beam - scanning electron microscopy},
  abstract = {<p>The structure degradation of commercial Lithium-ion battery (LIB) graphite anodes with different cycling numbers and charge rates was investigated by focused ion beam (FIB) and scanning electron microscopy (SEM). The cross-section image of graphite anode by FIB milling shows that cracks, resulted in the volume expansion of graphite electrode during long-term cycling, were formed in parallel with the current collector. The crack occurs in the bulk of graphite particles near the lithium insertion surface, which might derive from the stress induced during lithiation and de-lithiation cycles. Subsequently, crack takes place along grain boundaries of the polycrystalline graphite, but only in the direction parallel with the current collector. Furthermore, fast charge graphite electrodes are more prone to form cracks since the tensile strength of graphite is more likely to be surpassed at higher charge rates. Therefore, for LIBs long-term or high charge rate applications, the tensile strength of graphite anode should be taken into account.</p>},
  year = {2017},
  journal = {Journal of Power Sources},
  volume = {365},
  pages = {235 - 239},
  month = {01/2017},
  issn = {03787753},
  doi = {10.1016/j.jpowsour.2017.08.045},
  language = {eng},
}