@article{25250,
  keywords = {Ybacuo, Layers, Structure, Layer, Intermediate},
  author = {Ronald P Reade and Paul H Berdahl and Leonard W Schaper and Richard E Russo},
  title = {Multilayer YBaCuO structures using ion-assisted intermediate layers},
  abstract = {<p>Multilayer thin films of YBa<sub>2</sub>Cu<sub>3</sub>O<sub>7-δ</sub> (YBCO) were deposited <em>in situ</em> on yttria-stabilized zirconia (YSZ) and CeO<sub>2</sub> intermediate layers grown using ion-assisted pulsed-laser deposition. These structures were grown on amorphous SiO<sub>2</sub> dielectric layers. A critical current density of 3x10<sup>5</sup> A/cm<sup>2</sup> was obtained for a YBCO film grown on SiO<sub>2</sub>-coated Haynes Alloy 230 substrate. Improvement of the critical current density was obtained below 77 K by doping the YBCO with 10% Ag. Angular magnetoresistance measurements provide further information about the texture of this film.</p>},
  year = {1995},
  journal = {IEEE Transactions on Applied Superconductvity},
  volume = {5},
  pages = {2007-2010},
  month = {06/1995},
  issn = {1051-8223 },
  doi = {10.1109/77.402980},
  language = {eng},
}